caustic cracking

An Investigation on Interface Reaction Regularity for Caustic Stress Corrosion Cracking of Fe-Cr-Ni Alloy

Fe-Cr-Ni合金碱性应力腐蚀破裂界面反应规律的研究

The results showed that the corrosion weight loss rate of high Mn steel was distinctly greater than that of medium carbon chromium steel. The high Mn steel caustic embrittlement cracking was distinct in corrosion.

结果表明，高锰钢的平均腐蚀速率显著高于中碳铬合金钢，腐蚀过程中高锰钢有较严重的碱脆开裂现象。

Effect of cold work on the caustic stress corrosion cracking of alloy 800

冷加工对800合金抗碱性应力腐蚀破裂的影响

With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.

随着热强碱腐蚀时间的延长，高锰钢的冲击韧度明显降低，碱脆开裂是造成高锰钢冲击韧度下降的主要原因。

Study on regeneration for spent caustic of ethylene cracking by chemical precipitation

化学沉淀法再生乙烯裂解废碱液的研究

Influence of Some Processing Factors on Susceptibility to Caustic Stress Corrosion Cracking of Modified Alloy 800

某些加工因素对改性800合金碱性应力腐蚀破裂敏感性的影响

With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.

随着钢中含铬量的增加，试验材料的活性溶解腐蚀失重增大，但碱脆开裂的倾向减少。